Feature Introduction:
BVOH K5 is a support material that dissolves in water much faster. It can be completely dissolved in water or to an easily peelable state in thirty minutes, several times faster than typical PVA materials. Compared with them, it is also less sensitive to humidity. BVOH K5 is a high-quality support material for PLA, PETG, ABS, and TPU, making it applicable to printed products with complex structures.
Basic Physical Properties:
| BVOH K5 | Printed copy (horizontal printing of sample, 100% linear filling) | Injection molded parts | Test standards |
| Density (g/cm3) | 1.05 | ISO 1183 | |
| Melt index (g/10min) * 1 | 30-35 | ISO 1133 | |
| Thermal deformation temperature (℃) * 2 | 85 | ISO 75 | |
| Vicat softening temperature (℃) * 3 | 95 | ISO 306 | |
| Tensile strength (MPa) | 41 | ISO 527 | |
| Tensile elongation at break (%) | 11 | ||
| Bending strength (MPa) | 77 | ISO 178 | |
| Bending modulus (MPa) | 2600 | ||
| Notched impact strength (KJ/m2) | 39 | ISO 179 | |
| Notch impact strength (KJ/m2) | 20 | ||
*1. Test condition: temperature (T)=220 ℃; Mass (m)=10kg.
*2. Test condition: bending stress=0.45MPa; Heating rate=120 ℃/h.
*3. Test condition: load=10N; Heating rate=120 ℃/h.