Menu
Feature Introduction:
HIPS K5 is a colorant-free support material with good performance and easy printability, which is completely soluble in limonene. When used as a support material for multi-jet printing, it prints smoothly with a clean surface with similar thermal properties to ABS materials. It is also a good-performance printing consumable with a clean surface and greater impact resistance.
Basic Physical Properties:
| HIPS K5 | Printed copy (horizontal printing of sample, 100% linear filling) | Injection molded parts | Test standards |
| Density (g/cm3) | 1.04 | ISO 1183 | |
| Melt flow rate (MFR) 1 | 5-7 | ISO 1133 | |
| Heat deflection temperature(HDT)2 | 97 | ISO 75 | |
| Vicat softening temperature(VST)3 | 103 | ISO 306 | |
| Tensile strength (MPa) | 20-23 | ISO 527 | |
| Elongation at break(%) | 15-19 | ||
| Maximum force(Mpa) | 34-35 | ISO 178 | |
| Flexural modulus(Mpa) | 1700-1800 | ||
| Impact strength(KJ/m2) | 10-11 | ISO 179 | |
| Notch impact strength1(KJ/m2) | 19-23 | ||
*1. Test condition: temperature (T)=200 ℃; Mass (m)=5kg.
*2. Test condition: bending stress=0.45MPa; Heating rate=120 ℃/h.
*3. Test condition: load=10N; Heating rate=120 ℃/h.