PAHT K7CF LM

  • TOUGHNESS
  • STRENGTH
  • HEAT RESISTANCE
  • Printability
  • Water Absorption
  • Rigidity
CHOOSE DIAMETER
  • 1.75mm
  • 2.85mm
CHOOSE WEIGHT
  • 0.5kg
  • 1kg
  • 3kg
CHOOSE COLORS
COLOR:
  • Black

Feature Introduction:

PAHT K7CFLM is a PA12-based carbon fiber reinforced nylon material with low water absorption as well as a substantial increase in strength, stiffness, and heat deflection temperature. This high-performance material can be printed by a common printer with a heating platform. It is applicable to light parts with resistance to oil and wear, or requiring high strength. It is recommended to use printing nozzles with a diameter over 0.6mm made of wear-resistance materials.

Basic Physical Properties:

PAHT K7CF LMPrinted copy (horizontal printing of sample, 100% linear filling)Injection molded partsTest standards
Density (g/cm3)1.12ISO 1183
Melt flow rate (MFR) 120-25ISO 1133
Heat deflection temperature(HDT)2109 ISO 75
Vicat softening temperature(VST)3206 ISO 306
Tensile strength (MPa)70-72 ISO 527
Elongation at break(%)15-18 
Maximum force(Mpa)100-120 ISO 178
Flexural modulus(Mpa)3000-3800 
Impact strength(KJ/m2)30-40 ISO 179
Notch impact strength1(KJ/m2)4-6 

*1. Test condition: temperature (T)=270 ℃; Mass (m)=2.16kg.
*2. Test condition: bending stress=0.45MPa; Heating rate=120 ℃/h.
*3. Test condition: load=10N; Heating rate=120 ℃/h.