Feature Introduction:
PEKK K10IAM is a PEKK material with low crystallization speed. Supplied consumables and printed products are generally transparent and amorphous. With its inherent resistance to flame and temperature, and high strength, PEKK K10IAM prints products with high-quality interlayer adhesion, thus it is prone to print parts with higher-strength Z-axis than typical PEEK materials.
Basic Physical Properties:
PEKK K10IAM | Printed copy (horizontal printing of sample, 100% linear filling) | Injection molded parts | Test standards |
| Density (g/cm3) | 1.28 | ISO 1183 | |
| Melt flow rate (MFR) 1 | 6-8 | ISO 1133 | |
| Heat deflection temperature(HDT)2 | 150 | ISO 75 | |
| Vicat softening temperature(VST)3 | 157.8 | ISO 306 | |
| Tensile strength (MPa) | 80-100 | ISO 527 | |
| Elongation at break(%) | 4-6 | ||
| Maximum force(Mpa) | 140-170 | ISO 178 | |
| Flexural modulus(Mpa) | 2900-3300 | ||
| Impact strength(KJ/m2) | 50-60 | ISO 179 | |
| Notch impact strength1(KJ/m2) | 4-8 | ||
*1. Test condition: temperature (T)=380 ℃; Mass (m)=1kg.
*2. Test condition: bending stress=0.45MPa; Heating rate=120 ℃/h.
*3. Test condition: load=10N; Heating rate=120 ℃/h.