Feature Introduction:
PEEK K10IAS is a PEEK material devoted to improving interlayers’ bonding. The Z-axis strength of printed products is significantly enhanced to 80 MPa, while retaining PEEK materials’ characteristics, including high mechanical performance, resistance to heat, flame, and chemicals, and easy printability.
Basic Physical Properties:
| PEEK K10IAS | Printed copy (horizontal printing of sample, 100% linear filling) | Injection molded parts | Test standards |
| Density (g/cm3) | 1.28 | ISO 1183 | |
| Melt index (g/10min) * 1 | 10-15 | ISO 1133 | |
| Thermal deformation temperature (℃) * 2 | 202 | ISO 75 | |
| Vicat softening temperature (℃) * 3 | / | ISO 306 | |
| Tensile strength (MPa) | 80-85 | ISO 527 | |
| Tensile elongation at break (%) | 6-8 | ||
| Bending strength (MPa) | 120-130 | ISO 178 | |
| Bending modulus (MPa) | 4000-5000 | ||
| Notched impact strength (KJ/m2) | 48-55 | ISO 179 | |
| Notch impact strength (KJ/m2) | 8-12 | ||
*1. Test condition: temperature (T)=380 ℃; Mass (m)=5kg.
*2. Test condition: bending stress=0.45MPa; Heating rate=120 ℃/h.
*3. Test condition: load=10N; Heating rate=120 ℃/h.