Feature Introduction:
PEI K10Ultem1010 is a polyetherimide material applicable to 3D printing. It is characterized by multiple properties, including high strength and toughness, heat deflection temperature and Vicat softening temperature up to about 200°C, resistance to gasoline, various hydrocarbon solvents, dilute acids and alkalis, and flame retardancy grade up to UL94 V-0. It is widely applicable to concept modeling, functional prototypes, end-use components, such as food and drug packaging, high-temperature components, and medical equipment manufacturing.
Basic Physical Properties:
PEI K10 Ultem1010 | Printed copy (horizontal printing of sample, 100% linear filling) | Injection molded parts | Test standards |
| Density (g/cm3) | 1.28 | ISO 1183 | |
| Melt flow rate (MFR) 1 | 35-40 | ISO 1133 | |
| Heat deflection temperature(HDT)2 | 208 | ISO 75 | |
| Vicat softening temperature(VST)3 | 210 | ISO 306 | |
| Tensile strength (MPa) | 85-90 | ISO 527 | |
| Elongation at break(%) | 4-6 | ||
| Maximum force(Mpa) | 150-170 | ISO 178 | |
| Flexural modulus(Mpa) | 3800-4200 | ||
| Impact strength(KJ/m2) | 38-42 | ISO 179 | |
| Notch impact strength1(KJ/m2) | 4-6 | ||
*1. Test condition: temperature (T)=365 ℃; Mass (m)=5kg.
*2. Test condition: bending stress=0.45MPa; Heating rate=120 ℃/h.
*3. Test condition: load=10N; Heating rate=120 ℃/h.