Feature Introduction:
PLA K5T is a transparent material. With PLA materials’ environmental friendliness and printability, it is improved to be less fragile than other transparent PLA filament by specialized process adjustment, thus it is applicable to surface-finish and transparent models.
Basic Physical Properties:
| PLA K5T | Printed copy (horizontal printing of sample, 100% linear filling) | Injection molded parts | Test standards |
| Density (g/cm3) | 1.24 | ISO 1183 | |
| Melt flow rate (MFR) 1 | 4-8 | ISO 1133 | |
| Heat deflection temperature(HDT)2 | 62 | ISO 75 | |
| Vicat softening temperature(VST)3 | 61 | ISO 306 | |
| Tensile strength (MPa) | 50-56 | ISO 527 | |
| Elongation at break(%) | 6-10 | ||
| Maximum force(Mpa) | 80-85 | ISO 178 | |
| Flexural modulus(Mpa) | 2500-2700 | ||
| Impact strength(KJ/m2) | 21-26 | ISO 179 | |
| Notch impact strength1(KJ/m2) | 3-5 | ||
*1. Test condition: temperature (T)=190 ℃; Mass (m)=2.16kg.
*2. Test condition: bending stress=0.45MPa; Heating rate=120 ℃/h.
*3. Test condition: load=10N; Heating rate=120 ℃/h.