PLA K6

  • TOUGHNESS
  • STRENGTH
  • HEAT RESISTANCE
  • Printability
  • Rigidity
  • Z-axis strength
CHOOSE DIAMETER
  • 1.75mm
  • 2.85mm
CHOOSE WEIGHT
  • 0.5kg
  • 1kg
  • 3kg
CHOOSE COLORS
COLOR:
  • White
  • Yellow
  • Orange
  • Red
  • Purple
  • Green
  • Blue
  • Silver
  • Gray
  • Black

Feature Introduction:

PLA K6 is an upgraded PLA material with high toughness. The modified material is designed with high toughness in both injection molded and printed products. The impact strength of injection parts is more than 10 times that of raw materials; the unnotched impact strength of printed products is also more than 3 times that of injection products made by raw materials, and their notched impact strength is more than 6 times that of raw materials. Furthermore, it retains the edges of PLA printing, such as no warpage and great interlayer bonding, thus it is applicable to structural parts with higher engineering performance requirements.

Basic Physical Properties:

PLA K6Printed copy (horizontal printing of sample, 100% linear filling)Injection molded partsTest standards
Density (g/cm3)1.22-1.24ISO 1183
Melt flow rate (MFR) 14-6ISO 1133
Heat deflection temperature(HDT)254 ISO 75
Vicat softening temperature(VST)359 ISO 306
Tensile strength (MPa)34-38 ISO 527
Elongation at break(%)10-15 
Maximum force(Mpa)60-65 ISO 178
Flexural modulus(Mpa)2100-2400 
Impact strength(KJ/m2)65-100 ISO 179
Notch impact strength1(KJ/m2)25-35 

*1. Test condition: temperature (T)=190 ℃; Mass (m)=2.16kg.
*2. Test condition: bending stress=0.45MPa; Heating rate=120 ℃/h.
*3. Test condition: load=10N; Heating rate=120 ℃/h.