THE K6™ PLA FR

  • TOUGHNESS
  • STRENGTH
  • HEAT RESISTANCE
  • Printability
  • Water Absorption
  • Rigidity
CHOOSE DIAMETER
  • 1.75mm
  • 2.85mm
CHOOSE WEIGHT
  • 0.5kg
  • 1kg
CHOOSE COLORS
COLOR:
  • White
  • Black

Feature Introduction:

THE K6™ PLA FR is a modified PLA composite with flame retardancy and high toughness. Both injection molded and printed products are with high toughness and flame retardancy rating of UL94-V0. The elongation at break of injection molded parts is more than 5 times that of raw materials with PLA printing’s no warping and great interlayer bonding. Thus, it is applicable to printed products with higher engineering performance requirements, such as structural parts and flame retardant parts.

Basic Physical Properties:

THE K6™ PLA FRPrinted copy (horizontal printing of sample, 100% linear filling)Injection molded partsTest standards
Density (g/cm3)1.05ISO 1183
Melt flow rate (MFR) 130-35ISO 1133
Heat deflection temperature(HDT)285 ISO 75
Vicat softening temperature(VST)395 ISO 306
Tensile strength (MPa)41 ISO 527
Elongation at break(%)11 
Maximum force(Mpa)77 ISO 178
Flexural modulus(Mpa)2600 
Impact strength(KJ/m2)39 ISO 179
Notch impact strength1(KJ/m2)20 

*1. Test condition: temperature (T)=220 ℃; Mass (m)=10kg.
*2. Test condition: bending stress=0.45MPa; Heating rate=120 ℃/h.
*3. Test condition: load=10N; Heating rate=120 ℃/h.