Feature Introduction:
WOOD K5 is a PLA material with an optimized proportion of wood fibers, making printed products present a wood-like texture. It enhances the visual and textural vividness of printed products, such as crafts and decorative objects.
Basic Physical Properties:
| WOOD K5 | Printed copy (horizontal printing of sample, 100% linear filling) | Injection molded parts | Test standards |
| Density (g/cm3) | 1.22-1.24 | ISO 1183 | |
| Melt flow rate (MFR) 1 | 7-12 | ISO 1133 | |
| Heat deflection temperature(HDT)2 | 57 | ISO 75 | |
| Vicat softening temperature(VST)3 | 58 | ISO 306 | |
| Tensile strength (MPa) | 25-28 | ISO 527 | |
| Elongation at break(%) | 8-10 | ||
| Maximum force(Mpa) | 50-55 | ISO 178 | |
| Flexural modulus(Mpa) | 2200-2400 | ||
| Impact strength(KJ/m2) | 12-14 | ISO 179 | |
| Notch impact strength1(KJ/m2) | 3-4 | ||
*1. Test condition: temperature (T)=190 ℃; Mass (m)=2.16kg.
*2. Test condition: bending stress=0.45MPa; Heating rate=120 ℃/h.
*3. Test condition: load=10N; Heating rate=120 ℃/h.