Suggested Printing Parameters
| Nozzle temperature | 380 ~ 420℃ |
| Bed temperature | 100 ~ 150℃ |
| Bed modification | High temperature glue |
| Active cooling fan | ON,80%% |
| Layer height | 0.2mm |
| Shell thickness | ≥ 0.8mm |
| Print speed | 30~60mm/s |
Technical Data Sheet (TDS)
| Material Properties | Typical Value | Test Method |
|---|---|---|
| Glass transition temperature | ~338℃ | ISO 11357 |
| Melt flow rate (MFR)¹ | 20~25g/10min | ISO 1133 |
| Heat deflection temperature (HDT)² | 159℃(before annealing)/ 182℃(after annealing) | ISO 75 |
| Vicat softening temperature (VST)³ | 170℃(before annealing)/ ＞230℃(after annealing) | ISO 306 |
| Density | 1.28g/cm³ | ISO 1183 |
| Odor | Odorless | / |
| Solubility | Insoluble in water | / |
Select a color
Weight options:
: 250g, 500g, 1kg
THE K11™ PEEK PRO
THE K11™ PEEK PRO is an advanced PEEK alloy material engineered for enhanced 3D printing performance. Its slower crystallization rate, higher heat resistance, and exceptional strength make it a superior choice compared to traditional PEEK materials. This material is easier to print, less sensitive to environmental temperature variations, and delivers significantly higher Z-axis strength in printed parts.