THE K8™ TPU 65A

A slightly firmer grade that balances softness with enhanced printability. It maintains excellent elongation and a smooth finish, ideal for creating flexible parts that need a bit more structural integrity than 60A.

Strength Rebound% Toughness

Suggested Printing Parameters

Nozzle temperature240 ~ 250℃
Bed temperature35 ~ 55℃
Bed modificationPEI frosted board
Active cooling fanON,50~100%
Layer height0.2mm
Shell thickness≥ 0.8mm
Print speed20mm/s
Settings are based on a 0.4mm nozzle.

Technical Data Sheet (TDS)

Material Properties Typical Value Test Method
Melt flow rate (MFR)¹25~35g/10minISO 1133
Heat deflection temperature (HDT)²/ISO 75
Vicat softening temperature (VST)³/ISO 306
Density1.20~1.22g/cm³ISO 1183
Hardness62AGB/T 531.1
Resilience65%GB/T 1681-2009
OdorOdorless/
SolubilityInsoluble in water/

1. Test conditions: T= 210℃; m= 2.16kg.

2. Test conditions: 0.45MPa; 130℃/h.

TDS⇩
Brochure⇩